MasterKure CC 100WB (clear or white) is a water based wax emulsion compound for curing fresh moist plain concrete. It forms a flexible film which prevents concrete drying out during the critical early stages of hydration thus ensuring satisfactory curing of the concrete. MasterKure CC 100WB meets the requirements of AS 3799 1998,"Specification for Liquid Membrane-Forming Curing Compounds for Concrete" when applied at the recommended application rate.
MasterKure CC 100WB (clear or white) is not recommended for application when subsequent renders, toppings or coatings are to be applied.
MasterKure CC 100WB white is not recommended for coloured concrete finishes.
AS 3799-1998 specification requires that curing compounds achieve a minimum efficiency index of 90% in 72 hours.
Water retention efficiency conducted on MasterKure CC 100WB provided the following results.
Application Rate 5m²/litre
Efficiency Index >90%
Drying Time: Approximately 3 hours at 23°C
Note: The data shown is based on controlled laboratory tests. Reasonable variations from the results can be expected in practice due to field conditions.
The concrete shall be cured with MasterKure CC 100WB applied as soon as the concrete has set sufficiently so as not to be marred by the application. Formed surfaces shall be cured as soon as the forms have been stripped. Preparation of surfaces, quantities used, application procedures and installation precautions shall be followed in strict compliance as recommendations and directions.
Code | Item | Pack |
---|---|---|
10202 | MasterKure CC 100WB - Water Based Wax Emulsion Curing Compound 20L | 20L |
10203 | MasterKure CC 100WB - Water Based Wax Emulsion Curing Compound 200L | 200L |
MasterKure CC 100WB should be applied in one coat immediately after the final finishing operation as soon as the surface has hardened sufficiently to prevent marring.
The surface should be damp but with no free water on it. Delaying the application of MasterKure CC 100WB until the next day will allow considerable loss of moisture, reducing the effectiveness of the curing membrane.
Apply uniformly and thinly so as to form a continuous film. MasterKure CC 100WB is applied using a wide short nap roller, brush, or low-pressure spray. Do not dilute. MasterKure CC 100WB is supplied in clear or white pigmented to reduce heat absorption by the concrete.
Actual coverage depends on the texture and porosity of the surface. The recommended application rate is 5m²/litre.
Clean equipment immediately after use with hot water. If allowed to dry, use MasterSeal 955 to clean up.
MasterKure CC 100WB has a shelf life of approximately 12 months if stored in its original sealed container at moderate temperatures. Do not allow to freeze. Avoid as far as possible storage in direct sunlight and avoid long-term exposure to high temperatures.
For the full health and safety hazard information and how to safely handle and use this product, please make sure that you obtain a copy of the BASF Safety Data Sheet (SDS) from BASF office or website.